AISI/SAE 1018 Round Steel Bar
SKU: HC-1137082575032639488
AISI 1018 carbon steel bar has a chemical composition of carbon, chromium, manganese, molybdenum, phosphorus, sulfur and silicon. AISI 1018 carbon steel is a free machining grade that is the most commonly available grade around the world.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：haven@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
AISI 1018 carbon steel bar has a chemical composition of carbon, chromium, manganese, molybdenum, phosphorus, sulfur and silicon. AISI 1018 carbon steel is a free machining grade that is the most commonly available grade around the world. 1018 cold rolled steel bar is made of a general-purpose, low-carbon steel with good case hardening qualities. It is especially suited to cold forming and bending operations. 1018 steel is suitable for parts that require cold forming such as crimping, swaging, or bending. 1018 steel is mild steel with medium-low carbon content. AISI 1018 carbon steel is a free machining grade that is the most commonly available grade around the world. Although its mechanical properties are not very unique, it still can be easily formed, machined, welded and fabricated.
Specifications
Product Parameters
| Product Name | AISI/SAE 1018 Round Steel Bar | |||
| Standard | EN / DIN / JIS / ASTM / BS / ASME / AISI,etc. | |||
| Common Round Bar Specifications | 3.0 - 50.8 mm,Over 50.8 - 300mm | |||
| Flat Steel Common Specifications | 6.35x12.7mm,6.35x25.4mm,12.7x25.4mm | |||
| Hexagon Bar Common Specifications | AF5.8mm - 17mm | |||
| Square Bar Common Specifications | AF2mm - 14mm,AF6.35mm,9.5mm,12.7mm,15.98mm,19.0mm,25.4mm | |||
| Length | 1 - 6 meters,Size Accept Custom | |||
| Diameter(mm) | Hot Rolling R ound Bar | 25 - 600 | Cold Rolling Square Bar | 6 - 50.8 |
| Hot Rolling Square Bar | 21 - 54 | Cold Rolling Hexagon Bar | 9.5 - 65 | |
| Cold Rolling Round bar | 6 - 101.6 | Forged Rebar | 200 - 1000 | |
| Surface Process | Bright,Polished,Black | |||
| Other Services | Machining(cnc),Centerless Grinding(cg),Heat Treatment,Annealing,Pickling,Polishing,Rolling,Forging,Cutting,Bending,Small Machining,etc. | |||
Chemical Composition
| Carbon Steel | C | Fe | Mn | P | S |
|---|---|---|---|---|---|
| 1018 | 0.14 - 0.20 % | 98.81 - 99.26 % | 0.60 - 0.90 % | 0.040 % | 0.050 % |
Mechanical Properties
| Tensile Strength | Yield Strength | Elongation % | Hardness (Brinell) | Hardness (Rockwell B) |
|---|---|---|---|---|
| 440 MPa | 370 MPa | 22 | 126 | 71 |