A537 pressure vessel steel coil is made of heat treated carbon manganese silicon steel that is used in pressure vessel fabrication. There are 3 grades, which are Grade 1, Grade 2, and Grade 3.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：haven@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
A537 pressure vessel steel coil is made of heat treated carbon manganese silicon steel that is used in pressure vessel fabrication. There are 3 grades, which are Grade 1, Grade 2, and Grade 3. ASTM A537 pressure vessel steel coils , as a high-strength, high-quality steel, are widely used in petroleum, chemical industry, pressure vessels and other fields . The strength of A537 is much higher than that of ordinary steel, and it can maintain excellent stability in high-pressure and high-temperature environments. A537 steel coil gains extremely strong corrosion resistance and can adapt to various harsh environments after special anti-corrosion treatment. Besides, A537 steel is easy to solder, reducing product damage of soldering problems.
Specifications
Product Parameters
| Product Name | A537 Pressure Vessel Carbon Steel Coil |
| Production Process | Hot Rolling,Cold Rolling |
| Material Standards | AISI,ASTM,ASME,DIN,BS,EN,ISO,JIS,GOST,SAE,etc. |
| Width | 45mm-2200mm |
| Length | Custom Size |
| Thickness | Hot Rolling: 2.75mm-100mm Cold Rolling: 0.2mm-3mm |
| Delivery Conditions | Rolling,Annealing,Quenching,Tempered or Standard |
| Surface Process | Ordinary,Wire Drawing,Laminated Film |
Chemical Composition
| Standard | Thickness (mm) | C | Si | Mn | P | S | Cu | Ni | Cr | Mo |
|---|---|---|---|---|---|---|---|---|---|---|
| A537 | ≤ 40 mm | 0.24 | 0.15-0.50 | 0.70-1.35 | 0.035 | 0.035 | 0.35 | 0.25 | 0.25 | 0.08 |
| > 40 mm | 1.00-1.60 |
Mechanical Properties
| A537 | Thickness mm | Yield Mpa | Tensile Strength Mpa | Elongation % |
|---|---|---|---|---|
| Level 1 | ≤ 65 | 345 | 485-620 | 22 |
| 65-100 | 310 | 450-585 | - | |
| 100-150 | - | - | 18 | |
| Level 2 | ≤ 65 | 415 | 550-690 | 22 |
| 65-100 | 380 | 515-655 | 20 | |
| 100-150 | 315 | 485-620 | - | |
| Level 3 | ≤ 65 | 380 | 550-690 | 22 |
| 66-100 | 345 | 515-655 | 20 | |
| 101-150 | 275 | 485-620 | - |
Physical Performance
| Physical Performance | Metric | Imperial |
|---|---|---|
| Density | 7.80 g/cc | 0.282 lb/in³ |